产品描述

ULTEM PEI HU2110物性表

“Ultem HU2110 resin是一种聚酯酰亚胺(PEI)产品,含有的填充物为10%玻璃纤维增强材料,可以通过注射成型进行加工。
典型应用领域为:医疗/保健。
特性包括:
环保/绿色
可接触食品
生物相容”

10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant.
Property/特性
TYPICAL PROPERTIES (1)
MECHANICAL/机械性能
Value/值 Unit/单位 Standard/标准
Tensile Stress, yld, Type I / 抗张程度,屈服,类型I, 5 mm/min
114
MPa
ASTM D 638
Tensile Stress, brk, Type I / 抗张程度,断裂,类型I, 5 mm/min
115
MPa
ASTM D 638
Tensile Strain, yld, Type I / 拉伸伸长,屈服,类型I, 5 mm/min
3
%
ASTM D 638
Tensile Strain, brk, Type I / 拉伸伸长,断裂,类型I, 5 mm/min
3
%
ASTM D 638
Tensile Modulus / 拉伸模量, 5 mm/min
4610
MPa
ASTM D 638
Flexural Stress, yld / 挠曲强度, 屈服 , 1.3 mm/min, 50 mm span
225
MPa
ASTM D 790
Flexural Modulus / 挠曲模量, 1.3 mm/min, 50 mm span
6850
MPa
ASTM D 790
Tensile Stress, yield / 抗张程度,屈服, 5 mm/min
165
MPa
ISO 527
Tensile Stress, break / 抗张程度,断裂, 5 mm/min
165
MPa
ISO 527
Tensile Strain, yield / 拉伸伸长,屈服, 5 mm/min
2
%
ISO 527
Tensile Strain, break / 拉伸伸长,断裂, 5 mm/min
2
%
ISO 527
Tensile Modulus / 拉伸模量, 1 mm/min
9500
MPa
ISO 527
Flexural Stress, yield / 弯曲强度,屈服, 2 mm/min
228
MPa
ISO 178
Flexural Modulus / 挠曲模量, 2 mm/min
6890
MPa
ISO 178
IMPACT/冲击性能
Value/值 Unit/单位 Standard/标准
Izod Impact, notched / 悬臂梁缺口冲击强度, 23°C
48
J/m
ASTM D 256
Izod Impact, notched / 悬臂梁缺口冲击强度, -30°C
64
J/m
ASTM D 256
Instrumented IMPACT Total Energy / 装有测量仪表的落镖冲击总能量, 23°C
8
J
ASTM D 3763
Izod Impact, notched / 悬臂梁缺口冲击强度 80*10*4 +23°C
64
kJ/m2
ISO 180/1A
Izod Impact, notched / 悬臂梁缺口冲击强度 80*10*4 -30°C
70
kJ/m2
ISO 180/1A
Charpy(简支梁缺口冲击强度) 23°C, V-notch(V型切口) Edgew 80*10*4 sp=62mm
65
kJ/m2
ISO 179/1eA
THERMAL/热性能
Value/值 Unit/单位 Standard/标准
Vicat Softening Temp, Rate / 维卡软化温度,等级 B/50
220
°C
ASTM D 1525
HDT(?#32570;?#24418;温度), 1.82 MPa, 6.4 mm, unannealed (未退火)
207
°C
ASTM D 648
CTE(线形膨胀系数), -40°C to 40°C, flow(流动)
2.5E-05
1/°C
ASTM E 831
CTE(线形膨胀系数), -40°C to 40°C, xflow(横向)
5.E-05
1/°C
ASTM E 831
CTE(线形膨胀系数), -40°C to 40°C, flow(流动)
2.5E-05
1/°C
ISO 11359-2
CTE(线形膨胀系数), -40°C to 40°C, xflow(横向)
5.E-05
1/°C
ISO 11359-2
Vicat Softening Temp, Rate / 维卡软化温度,等级 B/50
220
°C
ISO 306
Vicat Softening Temp, Rate / 维卡软化温度,等级 B/120
213
°C
ISO 306
HDT(?#32570;?#24418;温度)/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
205
°C
ISO 75/Af
PHYSICAL/物理性能
Value/值 Unit/单位 Standard/标准
Specific Gravity / 比重
1.34
ASTM D 792
Mold Shrinkage / 收缩率, flow(流动), 3.2 mm (5)
0.2 – 0.4
%
SABIC Method
Melt Flow Rate / 熔流率,, 337°C/6.6 kgf
11.3
g/10 min
ASTM D 1238
Density / 密度
1.42
g/cm3
ISO 1183
Water Absorption / 吸水率, (23°C/sat)
0.9
%
ISO 62
Moisture Absorption / 吸水率, ?#33014;?(23°C / 50% RH)
0.5
%
ISO 62
Source GMD, last updated:2009/09/30
Processing/加工方法
Parameter
Injection Molding/注塑参数
Value/值 Unit/单位
Drying Temperature / 干燥温度
150
°C
Drying Time / 干燥时间
4 – 6
hrs
Drying Time (Cumulative) / 干燥时间(累积的)
24
hrs
Maximum Moisture Content / 最大含湿量
0.02
%
Melt Temperature / 熔体温度
350 – 400
°C
Nozzle Temperature / 注嘴温度
345 – 400
°C
Front – Zone 3 Temperature / 前区3温度
345 – 400
°C
Middle – Zone 2 Temperature / 中区2温度
340 – 400
°C
Rear – Zone 1 Temperature / 后区1温度
330 – 400
°C
Mold Temperature / 模具温度
135 – 165
°C
Back Pressure / 背压
0.3 – 0.7
MPa
Screw Speed / 螺杆速度
40 – 70
rpm
Shot to Cylinder Size / 每次注射量占料筒熔胶总量的百分比
40 – 60
%
Vent Depth / 排气?#21672;?#24230;
0.025 – 0.076
mm
Source GMD, last updated:2009/09/30