产品描述

ULTEM PEI 2100F物性表

“Ultem 2100F resin是一种聚酯酰亚胺(PEI)产品,含有的填充物为10% 玻璃纤维增强材料。可以通过注射成型进行加工。
应用领域包括食品接触应用和水管/管道/饮用水。
特性包括:
阻燃/额定火焰
环保/绿色
可接触食品”

10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). UL94 V0 listing. US FDA and European Food Contact approved. Effective June, 2007 this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HU2100.
Property/特性
TYPICAL PROPERTIES (1)
MECHANICAL/机械性能
Value/值 Unit/单位 Standard/标准
Taber Abrasion / 泰伯磨耗量, CS-17, 1 kg
15
mg/1000cy
SABIC Method
Tensile Stress, break / 抗张程度,断裂, 5 mm/min
115
MPa
ISO 527
Tensile Strain, break / 拉伸伸长,断裂, 5 mm/min
4
%
ISO 527
Tensile Modulus / 拉伸模量, 1 mm/min
4500
MPa
ISO 527
Flexural Stress, break / 弯曲强度,断裂, 2 mm/min
185
MPa
ISO 178
Flexural Modulus / 挠曲模量, 2 mm/min
4500
MPa
ISO 178
Hardness / 硬度, H358/30
140
MPa
ISO 2039-1
IMPACT/冲击性能
Value/值 Unit/单位 Standard/标准
Izod Impact, unnotched / 无缺口悬臂梁冲击 80*10*4 +23°C
30
kJ/m2
ISO 180/1U
Izod Impact, unnotched / 无缺口悬臂梁冲击 80*10*4 -30°C
30
kJ/m2
ISO 180/1U
Charpy Impact, notched /简支梁缺口冲击强度, 23°C
7
kJ/m2
ISO 179/2C
THERMAL/热性能
Value/值 Unit/单位 Standard/标准
Thermal Conductivity / 导热系数
0.24
W/m-°C
ISO 8302
CTE(线形膨胀系数), 23°C to 150°C, flow(流动)
2.6E-05
1/°C
ISO 11359-2
CTE(线形膨胀系数), 23°C to 150°C, xflow(横向)
6.E-05
1/°C
ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C
PASSES
IEC 60695-10-2
Vicat Softening Temp, Rate / 维卡软化温度,?#29123;?A/50
223
°C
ISO 306
Vicat Softening Temp, Rate / 维卡软化温度,?#29123;?B/50
212
°C
ISO 306
Vicat Softening Temp, Rate / 维卡软化温度,?#29123;?B/120
217
°C
ISO 306
HDT(?#32570;?#24418;温度)/Be, 0.45MPa Edgew 120*10*4 sp=100mm
210
°C
ISO 75/Be
HDT(?#32570;?#24418;温度)/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
205
°C
ISO 75/Ae
PHYSICAL/物理性能
Value/值 Unit/单位 Standard/标准
Mold Shrinkage on Tensile Bar / 收缩率, flow(流动) (2)
0.4 – 0.6
%
SABIC Method
Density / 密度
1.34
g/cm3
ISO 1183
Water Absorption / 吸水率, (23°C/sat)
1
%
ISO 62
Moisture Absorption / 吸水率, ?#33014;?(23°C / 50% RH)
0.6
%
ISO 62
Melt Volume Rate / 溶化体积流率, MVR at 360°C/5.0 kg
9
cm3/10 min
ISO 1133
ELECTRICAL/电气性能
Value/值 Unit/单位 Standard/标准
Volume Resistivity / 体积电阻率
1.E+15
Ohm-cm
IEC 60093
Surface Resistivity ROA / 表面电阻率
>1.E+15
Ohm
IEC 60093
Dielectric Strength, in oil / 耐电强度,在油中, 0.8 mm
34
kV/mm
IEC 60243-1
Dielectric Strength, in oil / 耐电强度,在油中, 1.6 mm
27
kV/mm
IEC 60243-1
Dielectric Strength, in oil / 耐电强度,在油中, 3.2 mm
15
kV/mm
IEC 60243-1
Relative Permittivity / 相对介电常数, 50/60 Hz
3
IEC 60250
Relative Permittivity / 相对介电常数, 1 MHz
2.9
IEC 60250
Dissipation Factor / 耗散因素, 50/60 Hz
0.0009
IEC 60250
Dissipation Factor / 耗散因素, 1 MHz
0.0025
IEC 60250
Dissipation Factor / 耗散因素, 2450 MHz
0.0046
IEC 60250
Comparative Tracking Index / 相比耐漏电起痕指数
150
V
IEC 60112
Comparative Tracking Index / 相比耐漏电起痕指数, M
100
V
IEC 60112
FLAME CHARACTERISTICS/火焰特性
Value/值 Unit/单位 Standard/标准
Glow Wire Flammability Index / 灼热丝易燃指数 960°C, passes at
3.2
mm
IEC 60695-2-12
Oxygen Index / 极限氧指数 (LOI)
46
%
ISO 4589
Source GMD, last updated:10/11/2006
Processing/加工方法
Parameter
Injection Molding/注塑参数
Value/值 Unit/单位
Drying Temperature / 干燥温度
150
°C
Drying Time / 干燥时间
4 – 6
hrs
Maximum Moisture Content / 最大含湿量
0.02
%
Melt Temperature / 熔体温度
370 – 410
°C
Nozzle Temperature / 注嘴温度
350 – 405
°C
Front – Zone 3 Temperature / 前区3温度
360 – 415
°C
Middle – Zone 2 Temperature / 中区2温度
350 – 405
°C
Rear – Zone 1 Temperature / 后区1温度
340 – 395
°C
Hopper Temperature / 料筒温度
80 – 120
°C
Mold Temperature / 模具温度
140 – 180
°C
Source GMD, last updated:10/11/2006