产品描述

ULTEM PEI 1110V物性表

Enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card.

TYPICAL PROPERTIES (1)
MECHANICAL机械性能
Value Unit Standard
Tensile Stress, yld, Type I, 5 mm/min / 抗张程度,屈服,类型I,5 mm/min
110
MPa
ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min / 抗张程度,断裂,类型I,5 mm/min
85
MPa
ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min / 拉伸伸长,屈服,类型I,5 mm/min
7
%
ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min / 拉伸伸长,断裂,类型I,5 mm/min
70
%
ASTM D 638
Tensile Modulus, 5 mm/min / 拉伸模量,5 mm/min
3720
MPa
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距
165
MPa
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距
3720
MPa
ASTM D 790
Tensile Stress, yield 5 mm/min / 抗张程度,屈服, 5 mm/min
110
MPa
ISO 527
Tensile Stress, break, 5 mm/min / 抗张程度,断裂,5mm/min
80
MPa
ISO 527
Tensile Strain, yield, 5 mm/min / 拉伸伸长,屈服,5mm/min
6
%
ISO 527
Tensile Strain, break, 5 mm/min / 拉伸伸长,断裂,5mm/min
60
%
ISO 527
Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min
3500
MPa
ISO 527
Flexural Stress, yield, 2 mm/min / 弯曲强度,屈服,2 mm/min
140
MPa
ISO 178
Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min
3300
MPa
ISO 178
IMPACT
Value Unit Standard
Izod Impact, unnotched, 23°C / 无缺口悬臂梁冲击 23°C
2100
J/m
ASTM D 4812
Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C
56
J/m
ASTM D 256
Izod IMPACT, notched, -30°C / 悬壁梁缺口冲击强度, -30°C
56
J/m
ASTM D 256
Instrumented Impact Total Energy, 23°C / 仪表控制抗冲击总能量,23°C
28
J
ASTM D 3763
Izod Impact, unnotched 80*10*4 +23°C
NB
kJ/m2
ISO 180/1U
Izod Impact, unnotched 80*10*4 -30°C
NB
kJ/m2
ISO 180/1U
Izod IMPACT, notched 80*10*4 +23°C / 悬壁梁缺口冲击强度,80*10*4 +23°C
4
kJ/m2
ISO 180/1A
Izod IMPACT, notched 80*10*4 -30°C / 悬壁梁缺口冲击强度,80*10*4 -30°C
4
kJ/m2
ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm / 简支梁缺口冲击强度,23°C,C80*10*4 sp=62mm
5
kJ/m2
ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm / 简支梁缺口冲击强度,-30°C,C80*10*4 sp=62mm
5
kJ/m2
ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm
NB
kJ/m2
ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm
NB
kJ/m2
ISO 179/1eU
THERMAL
Value Unit Standard
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
219
°C
ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed / ?#32570;?#24418;温度,0.45 MPa, 3.2 mm,未退火
207
°C
ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed / ?#32570;?#24418;温度,1.82 MPa, 3.2mm,未退火
197
°C
ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed / ?#32570;?#24418;温度,1.82 MPa, 6.4 mm, 未退火
199
°C
ASTM D 648
CTE, -40°C to 150°C, flow
5.5E-05
1/°C
ASTM E 831
CTE, -40°C to 150°C, xflow
5.5E-05
1/°C
ASTM E 831
CTE, 23°C to 150°C, flow
5.E-05
1/°C
ISO 11359-2
CTE, 23°C to 150°C, xflow
5.E-05
1/°C
ISO 11359-2
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
200
°C
ISO 306
Vicat Softening Temp, Rate B/120 / 维卡软化温度,B级/120
205
°C
ISO 306
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm / ?#32570;?#24418;温度,1.8 MPa, 未退火, 100 mm 跨距
185
°C
ISO 75/Ae
PHYSICAL
Value Unit Standard
Specific Gravity/比重
1.36
ASTM D 792
Mold Shrinkage, flow, 3.2 mm / 模塑收缩量,流动,3.2 mm
0.4 – 0.6
%
SABIC Method
Melt Flow Rate / 熔流率, 337°C/6.6 kgf
16
g/10 min
ASTM D 1238
Density/密度
1.36
g/cm3
ISO 1183
Water Absorption, (23°C/sat) / 吸水率, (23°C/sat)
1.2
%
ISO 62
Moisture Absorption (23°C / 50% RH) / 吸水率, ?#33014;?(23°C / 50% RH)
0.65
%
ISO 62
Melt Volume Rate, MVR at 360°C/5.0 kg
21
cm3/10 min
ISO 1133
ELECTRICAL
Value Unit Standard
Volume Resistivity/体积电阻率
1.E+15
Ohm-cm
IEC 60093
Surface Resistivity, ROA / 表面电阻率
>1.E+15
Ohm
IEC 60093
Dielectric Strength, in oil, 3.2 mm / 耐电强度,在油中,3.2mm
17.2
kV/mm
IEC 60243-1
Relative Permittivity, 50/60 Hz / 相对介电常数,50/60 Hz
3.5
IEC 60250
Dissipation Factor, 50/60 Hz / 耗散因素,50/60 Hz
0.0016
IEC 60250
Comparative Tracking Index / 漏电起痕指数
175
V
IEC 60112
Comparative Tracking Index / 漏电起痕指数, M
125
V
IEC 60112
FLAME CHARACTERISTICS
Value Unit Standard
UL Recognized, 94V-1 Flame Class Rating (3) / UL认可,94V-1 阻燃等级(3)
0.75
mm
UL 94
UL Recognized, 94V-0 Flame Class Rating (3) / UL认可,94V-0 阻燃等级(3)
0.75
mm
UL 94
UL Recognized, 94-5VA Rating (3) / UL认可,94-5VA 阻燃等级(3)
3
mm
UL 94
Source GMD, last updated:11/03/2007
Processing
Parameter
Injection Molding
Value Unit
Drying Temperature / 干燥温度
150
°C
Drying Time / 干燥时间
4 – 6
hrs
Drying Time (Cumulative) / 干燥时间(累积?#27169;?/div>
24
hrs
Maximum Moisture Content / 最大含湿量
0.02
%
Melt Temperature / 熔体温度
350 – 400
°C
Nozzle Temperature / 注嘴温度
345 – 400
°C
Front – Zone 3 Temperature / 前区3温度
345 – 400
°C
Middle – Zone 2 Temperature / 中区2温度
340 – 400
°C
Rear – Zone 1 Temperature / 后区1温度
330 – 400
°C
Mold Temperature / 模具温度
135 – 165
°C
Back Pressure / 背压
0.3 – 0.7
MPa
Screw Speed / 螺杆速度
40 – 70
rpm
Shot to Cylinder Size / 每次注射量占料筒熔胶总量的百分比
40 – 60
%
Vent Depth / 排气?#21672;?#24230;
0.025 – 0.076
mm
Source GMD, last updated:11/03/2007