产品描述

ULTEM PEI 1040P物性表

Enhanced Flow Polyetherimide (Tg 217C) in 350 micron powder. ECO Conforming.
相关色号:1040P-1000

TYPICAL PROPERTIES (1)
MECHANICAL机械性能
Value Unit Standard
Tensile Stress, yld, Type I, 5 mm/min / 抗张程度,屈服,类型I,5 mm/min
96
MPa
ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min / 抗张程度,断裂,类型I,5 mm/min
96
MPa
ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min / 拉伸伸长,屈服,类型I,5 mm/min
5
%
ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min / 拉伸伸长,断裂,类型I,5 mm/min
10
%
ASTM D 638
Tensile Modulus, 5 mm/min / 拉伸模量,5 mm/min
3440
MPa
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距
3447
MPa
ASTM D 790
Flexural Stress, yld, 2.6 mm/min, 100 mm span
158
MPa
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距
3400
MPa
ASTM D 790
Tensile Stress, yield 5 mm/min / 抗张程度,屈服, 5 mm/min
90
MPa
ISO 527
Tensile Stress, break, 5 mm/min / 抗张程度,断裂,5mm/min
90
MPa
ISO 527
Tensile Strain, yield, 5 mm/min / 拉伸伸长,屈服,5mm/min
5
%
ISO 527
Tensile Strain, break, 5 mm/min / 拉伸伸长,断裂,5mm/min
10
%
ISO 527
Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min
3000
MPa
ISO 527
Flexural Stress, yield, 2 mm/min / 弯曲强度,屈服,2 mm/min
150
MPa
ISO 178
Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min
3000
MPa
ISO 178
IMPACT
Value Unit Standard
Izod Impact, unnotched, 23°C / 无缺口悬臂梁冲击 23°C
469
J/m
ASTM D 4812
Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C
21
J/m
ASTM D 256
Izod IMPACT, notched, -30°C / 悬壁梁缺口冲击强度, -30°C
20
J/m
ASTM D 256
Instrumented Impact Total Energy, 23°C / 仪表控制抗冲击总能量,23°C
30
J
ASTM D 3763
Izod IMPACT, notched 80*10*4 +23°C / 悬壁梁缺口冲击强度,80*10*4 +23°C
NB
kJ/m2
ISO 180/1A
Izod IMPACT, notched 80*10*4 -30°C / 悬壁梁缺口冲击强度,80*10*4 -30°C
NB
kJ/m2
ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm / 简支梁缺口冲击强度,23°C,C80*10*4 sp=62mm
5
kJ/m2
ISO 179/1eA
THERMAL
Value Unit Standard
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
205
°C
ASTM D 1525
HDT, 1.82 MPa, 6.4 mm, unannealed / ?#32570;?#24418;温度,1.82 MPa, 6.4 mm, 未退火
196
°C
ASTM D 648
CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动
5.5E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向
5.5E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动
5.5E-05
1/°C
ISO 11359-2
CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向
5.5E-05
1/°C
ISO 11359-2
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
211
°C
ISO 306
Vicat Softening Temp, Rate B/120 / 维卡软化温度,B级/120
212
°C
ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm / ?#32570;?#24418;温度,1.8 MPa, 未退火,80*10*4, 64.0 mm 跨距
190
°C
ISO 75/Af
PHYSICAL
Value Unit Standard
Specific Gravity/比重
1.27
ASTM D 792
Mold Shrinkage, flow, 3.2 mm / 模塑收缩量,流动,3.2 mm
0.5 – 0.7
%
SABIC Method
Melt Flow Rate / 熔流率, 295°C/6.6 kgf
6.6
g/10 min
ASTM D 1238
Density/密度
1.27
g/cm3
ISO 1183
Water Absorption, (23°C/sat) / 吸水率, (23°C/sat)
1.25
%
ISO 62
Moisture Absorption (23°C / 50% RH) / 吸水率, ?#33014;?(23°C / 50% RH)
0.7
%
ISO 62
Melt Volume Rate, MVR at 220°C/5.0 kg
10
cm3/10 min
ISO 1133
Source GMD, last updated:02/13/2007