产品描述

NORYL GTX GTX974物性表

NORYL GTX974 is a material especially designed for in- or on-line painted bodypanels and fenders in particular. This material combines impact performance with conductivity for electro-static painting in an unique way.

TYPICAL PROPERTIES (1)
MECHANICAL机械性能
 Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min / 抗拉强度,屈服,类型I,50 mm/min
55
MPa
ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min / 抗拉强度, 断裂, 类型I, 50 mm/min
50
MPa
ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min / 拉伸伸长, 屈服, 类型I, 50 mm/min
5
%
ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min / 拉伸伸长,断裂,类型I, 50 mm/min
50
%
ASTM D 638
Tensile Modulus, 50 mm/min / 拉伸模量,50 mm/min
2050
MPa
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距
80
MPa
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距
2050
MPa
ASTM D 790
Tensile Stress, yield 50 mm/min / 抗张程度，屈服, 50 mm/min
50
MPa
ISO 527
Tensile Stress, break, 50 mm/min / 抗张程度,断裂,50mm/min
45
MPa
ISO 527
Tensile Strain, yield, 50 mm/min / 拉伸伸长,屈服,,50mm/min
4
%
ISO 527
Tensile Strain, break, 50 mm/min / 拉伸伸长,断裂,50mm/min
30
%
ISO 527
Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min
2000
MPa
ISO 527
Flexural Stress, yield, 2 mm/min / 弯曲强度,屈服,2 mm/min
75
MPa
ISO 178
Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min
1900
MPa
ISO 178
IMPACT
 Value Unit Standard
Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C
180
J/m
ASTM D 256
Izod IMPACT, notched, -30°C / 悬壁梁缺口冲击强度, -30°C
120
J/m
ASTM D 256
Instrumented Impact Total Energy, 23°C / 仪表控制抗冲击总能量，23°C
50
J
ASTM D 3763
Izod IMPACT, notched 80*10*4 +23°C / 悬壁梁缺口冲击强度，80*10*4 +23°C
17
kJ/m2
ISO 180/1A
Izod IMPACT, notched 80*10*4 -30°C / 悬壁梁缺口冲击强度，80*10*4 -30°C
10
kJ/m2
ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm / 简支梁缺口冲击强度，23°C，C80*10*4 sp=62mm
18
kJ/m2
ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm / 简支梁缺口冲击强度，-30°C，C80*10*4 sp=62mm
10
kJ/m2
ISO 179/1eA
THERMAL
 Value Unit Standard
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
180
°C
ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed / ?#32570;?#24418;温度,0.45 MPa, 3.2 mm,未退火
180
°C
ASTM D 648
CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动
9.E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向
1.E-04
1/°C
ASTM E 831
CTE, 23°C to 60°C, flow / 线形膨胀系数,23°C 到60°C,流动
1.E-04
1/°C
ISO 11359-2
CTE, 23°C to 60°C, xflow / 线形膨胀系数,23°C 到60°C,横向
9.E-05
1/°C
ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C
PASSES
–
IEC 60695-10-2
Vicat Softening Temp, Rate A/50 / 维卡软化温度 A级/50
230
°C
ISO 306
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
175
°C
ISO 306
Vicat Softening Temp, Rate B/120 / 维卡软化温度,B级/120
180
°C
ISO 306
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm / ?#32570;?#24418;温度，0.45 MPa, 未退火, 100 mm 跨距
175
°C
ISO 75/Be
PHYSICAL
 Value Unit Standard
Specific Gravity/比重
1.08
–
ASTM D 792
Mold Shrinkage, flow, 3.2 mm / 模塑收缩量，流动，3.2 mm
1.3 – 1.6
%
SABIC Method
Mold Shrinkage, xflow, 3.2 mm / 模塑收缩量，横向，3.2 mm
1.1 – 1.4
%
SABIC Method
Melt Flow Rate / 熔流率, 280°C/5.0 kgf
10
g/10 min
ASTM D 1238
Density/密度
1.08
g/cm3
ISO 1183
Water Absorption, (23°C/sat) / 吸水率, (23°C/sat)
4.2
%
ISO 62
Moisture Absorption (23°C / 50% RH) / 吸水率, ?#33014;?(23°C / 50% RH)
1.2
%
ISO 62
Melt Volume Rate, MVR at 280°C/5.0 kg
12
cm3/10 min
ISO 1133
ELECTRICAL
 Value Unit Standard
Volume Resistivity/体积电阻率
1.E+03 – 1.E+04
Ohm-cm
SABIC Method
FLAME CHARACTERISTICS
 Value Unit Standard
UL Recognized, 94HB Flame Class Rating (3) / UL认可，94HB 阻燃等级(3)
1.5
mm
UL 94
UL Recognized, 94HB Flame Class Rating 2nd value (3)
3
mm
UL 94
Source GMD, last updated:06/25/2007
Processing
Parameter
Injection Molding
 Value Unit
Drying Temperature / 干燥温度
100 – 120
°C
Drying Time / 干燥时间
2 – 3
hrs
Maximum Moisture Content / 最大含湿量
0.07
%
Melt Temperature / 熔体温度
290 – 320
°C
Nozzle Temperature / 注嘴温度
280 – 310
°C
Front – Zone 3 Temperature / 前区3温度
290 – 320
°C
Middle – Zone 2 Temperature / 中区2温度
280 – 300
°C
Rear – Zone 1 Temperature / 后区1温度
260 – 280
°C
Hopper Temperature / 料筒温度
60 – 80
°C
Mold Temperature / 模具温度
80 – 120
°C
Sour ce GMD, last updated:06/25/2007