NORYL GTX GTX6203物性表

NORYL GTX6203 is a 20% talc filled material with superior dimensional stability, excellent processability and surface appearance.

TYPICAL PROPERTIES (1)
MEC HANICAL机械性能
Value Unit Standard
Tensile Stress, yld, Type I, 5 mm/min / 抗张程度,屈服,类型I,5 mm/min
65
MPa
ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min / 抗张程度,断裂,类型I,5 mm/min
65
MPa
ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min / 拉伸伸长,屈服,类型I,5 mm/min
3
%
ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min / 拉伸伸长,断裂,类型I,5 mm/min
3
%
ASTM D 638
Tensile Modulus, 5 mm/min / 拉伸模量,5 mm/min
4600
MPa
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距
100
MPa
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距
3800
MPa
ASTM D 790
Tensile Stress, yield 50 mm/min / 抗张程度,屈服, 50 mm/min
60
MPa
ISO 527
Tensile Stress, break, 50 mm/min / 抗张程度,断裂,50mm/min
60
MPa
ISO 527
Tensile Strain, yield, 5 mm/min / 拉伸伸长,屈服,5mm/min
2.5
%
ISO 527
Tensile Strain, break, 5 mm/min / 拉伸伸长,断裂,5mm/min
10
%
ISO 527
Tensile Strain, break, 50 mm/min / 拉伸伸长,断裂,50mm/min
10
%
ISO 527
Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min
4900
MPa
ISO 527
Flexural Stress, yield, 2 mm/min / 弯曲强度,屈服,2 mm/min
90
MPa
ISO 178
Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min
4000
MPa
ISO 178
IMPACT
Value Unit Standard
Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C
60
J/m
ASTM D 256
Izod IMPACT, notched, -30°C / 悬壁梁缺口冲击强度, -30°C
50
J/m
ASTM D 256
Instrumented Impact Total Energy, 23°C / 仪表控制抗冲击总能量,23°C
10
J
ASTM D 3763
Izod Impact, unnotched 80*10*4 +23°C
50
kJ/m2
ISO 180/1U
Izod IMPACT, notched 80*10*4 +23°C / 悬壁梁缺口冲击强度,80*10*4 +23°C
6
kJ/m2
ISO 180/1A
Izod IMPACT, notched 80*10*4 -30°C / 悬壁梁缺口冲击强度,80*10*4 -30°C
5
kJ/m2
ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm / 简支梁缺口冲击强度,23°C,C80*10*4 sp=62mm
5
kJ/m2
ISO 179/1eA
THERMAL
Value Unit Standard
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
185
°C
ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed / ?#32570;?#24418;温度,0.45 MPa, 3.2 mm,未退火
190
°C
ASTM D 648
CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动
6.E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向
7.8E-05
1/°C
ASTM E 831
Thermal Conductivity / 导热系数
0.26
W/m-°C
ISO 8302
CTE, 23°C to 80°C, flow
7.5E-05
1/°C
ISO 11359-2
CTE, 23°C to 80°C, xflow
9.E-05
1/°C
ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C
PASSES
IEC 60695-10-2
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
190
°C
ISO 306
Vicat Softening Temp, Rate B/120 / 维卡软化温度,B级/120
190
°C
ISO 306
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm / ?#32570;?#24418;温度,0.45 MPa, 未退火, 100 mm 跨距
190
°C
ISO 75/Be
PHYSICAL
Value Unit Standard
Specific Gravity/比重
1.25
ASTM D 792
Mold Shrinkage, flow, 3.2 mm / 模塑收缩量,流动,3.2 mm
0.6 – 0.9
%
SABIC Method
Mold Shrinkage, xflow, 3.2 mm / 模塑收缩量,横向,3.2 mm
0.6 – 0.9
%
SABIC Method
Melt Flow Rate / 熔流率, 280°C/5.0 kgf
20
g/10 min
ASTM D 1238
Density/密度
1.24
g/cm3
ISO 1183
Water Absorption, (23°C/sat) / 吸水率, (23°C/sat)
3.2
%
ISO 62
Moisture Absorption (23°C / 50% RH) / 吸水率, ?#33014;?(23°C / 50% RH)
1.1
%
ISO 62
Melt Volume Rate, MVR at 280°C/5.0 kg
20
cm3/10 min
ISO 1133
Source GMD, last updated:06/25/2007
Processing
Parameter
Injection Molding
Value Unit
Drying Temperature / 干燥温度
100 – 110
°C
Drying Time / 干燥时间
2 – 3
hrs
Maximum Moisture Content / 最大含湿量
0.07
%
Melt Temperature / 熔体温度
280 – 300
°C
Nozzle Temperature / 注嘴温度
270 – 290
°C
Front – Zone 3 Temperature / 前区3温度
280 – 300
°C
Middle – Zone 2 Temperature / 中区2温度
270 – 290
°C
Rear – Zone 1 Temperature / 后区1温度
260 – 280
°C
Hopper Temperature / 料筒温度
60 – 80
°C
Mold Temperature / 模具温度
80 – 100
°C
Sourc e GMD, last updated:06/25/2007