NORYL GTX 731A物性表

TYPICAL PROPERTIES (1)
MECHANICAL 机械性能
Value Unit Standard
Taber Abrasion, CS-17, 1 kg / 泰伯磨耗量, CS-17, 1 kg
20
mg/1000cy
SABIC Method
Tensile Stress, yield 50 mm/min / 抗张程度,屈服, 50 mm/min
55
MPa
ISO 527
Tensile Stress, break, 50 mm/min / 抗张程度,断裂,50mm/min
50
MPa
ISO 527
Tensile Strain, yield, 50 mm/min / 拉伸伸长,屈服,,50mm/min
5
%
ISO 527
Tensile Strain, break, 50 mm/min / 拉伸伸长,断裂,50mm/min
30
%
ISO 527
Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min
2300
MPa
ISO 527
Flexural Stress, yield, 2 mm/min / 弯曲强度,屈服,2 mm/min
75
MPa
ISO 178
Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min
2200
MPa
ISO 178
Hardness, H358/30 / 球压硬度,H358/30
100
MPa
ISO 2039-1
IMPACT
Value Unit Standard
Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C
200
J/m
ASTM D 256
Izod IMPACT, notched, -40°C / 悬壁梁缺口冲击强度,-40°C
140
J/m
ASTM D 256
Izod IMPACT, notched 80*10*4 +23°C / 悬壁梁缺口冲击强度,80*10*4 +23°C
15
kJ/m2
ISO 180/1A
Izod IMPACT, notched 80*10*4 -30°C / 悬壁梁缺口冲击强度,80*10*4 -30°C
5
kJ/m2
ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm / 简支梁缺口冲击强度,23°C,C80*10*4 sp=62mm
15
kJ/m2
ISO 179/1eA
Charpy Impact, notched, 23°C
15
kJ/m2
ISO 179/2C
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm / 简支梁缺口冲击强度,-30°C,C80*10*4 sp=62mm
5
kJ/m2
ISO 179/1eA
THERMAL
Value Unit Standard
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
146
°C
ASTM D 1525
Thermal Conductivity / 导热系数
0.22
W/m-°C
ISO 8302
CTE, 23°C to 80°C, flow
6.E-05
1/°C
ISO 11359-2
CTE, 23°C to 80°C, xflow
7.E-05
1/°C
ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C
PASSES
IEC 60695-10-2
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
130
°C
ISO 306
Vicat Softening Temp, Rate B/120 / 维卡软化温度,B级/120
135
°C
ISO 306
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm / ?#32570;?#24418;温度,0.45 MPa, 未退火, 100 mm 跨距
130
°C
ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm / ?#32570;?#24418;温度,1.8 MPa, 未退火, 100 mm 跨距
115
°C
ISO 75/Ae
PHYSICAL
Value Unit Standard
Specific Gravity/比重
1.06
ASTM D 792
Water Absorption, 24 hours / 吸水率, 24小时
0.07
%
ASTM D 570
Water Absorption, equilibrium, 100°C / 吸水率,?#33014;猓?00°C
0.3
%
ASTM D 570
Mold Shrinkage on Tensile Bar, flow (2) / 收缩率,流动
0.5 – 0.7
%
SABIC Method
Density/密度
1.06
g/cm3
ISO 1183
Water Absorption, (23°C/sat) / 吸水率, (23°C/sat)
0.14
%
ISO 62
Moisture Absorption (23°C / 50% RH) / 吸水率, ?#33014;?(23°C / 50% RH)
0.06
%
ISO 62
Melt Volume Rate, MVR at 280°C/5.0 kg
7
cm3/10 min
ISO 1133
ELECTRICAL
Value Unit Standard
Dielectric Strength, shorttime, 3.2 mm
22
kV/mm
ASTM D 149
Volume Resistivity/体积电阻率
1.E+15
Ohm-cm
IEC 60093
Relative Permittivity, 50/60 Hz / 相对介电常数,50/60 Hz
2.7
IEC 60250
Relative Permittivity, 1 MHz / 相对介电常数,1 MHz
2.6
IEC 60250
Dissipation Factor, 50/60 Hz / 耗散因素,50/60 Hz
0.0004
IEC 60250
Dissipation Factor, 1 MHz / 耗散因素,1 MHz
0.0009
IEC 60250
FLAME CHARACTERISTICS
Value Unit Standard
UL Recognized, 94HB Flame Class Rating (3) / UL认可,94HB 阻燃等级(3)
1.5
mm
UL 94
UL Recognized, 94HB Flame Class Rating 2nd value (3)
3
mm
UL 94
Oxygen Index (LOI) / 极限氧指数
24
%
ISO 4589
Source GMD, last updated:05/18/1989
Processing
Parameter
Injection Molding
Value Unit
Drying Temperature / 干燥温度
100 – 120
°C
Drying Time / 干燥时间
2 – 3
hrs
Melt Temperature / 熔体温度
280 – 300
°C
Nozzle Temperature / 注嘴温度
260 – 280
°C
Front – Zone 3 Temperature / 前区3温度
280 – 300
°C
Middle – Zone 2 Temperature / 中区2温度
260 – 280
°C
Rear – Zone 1 Temperature / 后区1温度
240 – 260
°C
Hopper Temperature / 料筒温度
60 – 80
°C
Mold Temperature / 模具温度
80 – 120
°C
Sour ce GMD, last updated:05/18/1989